Rilsamid® AESN Noir P40 TL
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | Arkema |
| Trademark: | Rilsamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UuDsTY_Rilsamid-AESN-Noir-P40-TL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsamid ® AESN Noir P40 TL is a black coloured polyamide. This grade is plasticized and designed for tube extrusion. AESN Noir P40 TL falls into the PA12-PHL category according to DIN 73378. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Additive |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (235°C/5.0 kg) | 10.0 | cm³/10min | ISO 11357 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 70 | ||
| Shore D, 15 sec | 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 445 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 27.0 | MPa | |
| Break | 47.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 27 | % | |
| Break | > 200 | % | |
| Flexural Modulus | 350 to 450 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 9.00 | mg | ISO 9352 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | No Break | ||
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 174 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PA12-P, EHL, 22-004 | ISO 1874 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Melt Temperature | 210 to 260 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-403-M-G20 HF | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Axiall PVC 3121 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| KOPLA PA66 KDU1021 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| Karina YELLOW COLOR CONCENTRATE -E 02/ 5-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| EPAMOULD 665D30 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |