AGILITY™ 1000 Performance LDPE
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | AGILITY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UtgrEG_AGILITY-1000-Performance-LDPE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AGILITY™ 1000 Performance LDPE is a high pressure LDPE resin designed specifically to run at faster output rates on blown film lines in blends with LLDPE resins while maintaining bubble stability. AGILITY™ 1000 Performance LDPE also has excellent shrink and good optics performance in blends with LLDPE resins. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.18 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Film Puncture Resistance (51 µm) | 6.04 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 51 µm | 221 | MPa | ASTM D882 |
| 2% secant, MD : 51 µm | 200 | MPa | ASTM D882 |
| 1% secant, TD : 51 µm | 254 | MPa | ASTM D882 |
| 2% secant, TD : 51 µm | 225 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 12.4 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 12.7 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 28.0 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 26.8 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 390 | % | ASTM D882 |
| TD : Fracture, 51 µm | 560 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | 270 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 51 µm | 180 | g | ASTM D1922 |
| TD : 51 µm | 200 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 109 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.8 µm) | 61 | ASTM D2457 | |
| Clarity (50.8 µm) | 92.0 | ASTM D1746 | |
| Haze (50.8 µm) | 10 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| Fabrication Conditions For Blown Film: Screw Size: 3.5 in. (88.9 mm), 30:1 L/D Die Gap: 30 mil (1.78mm) Melt Temperature: 423°F (217°C) Output: 10 lb/hr/in. of die circumference Die Diameter: 8 in. Blow-Up Ratio: 2.5 to 1 Screw Speed: 45.3 rpm Frost Line Height: 31 in. (787 mm) |
| Note Message | |
|---|---|
| 1 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ebalta GM 955-40 / Comp. A+B | Ebalta Kunststoff GmbH | PUR, Unspecified | Ebalta |
| Geon™ Vinyl Flexible B6DT0 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Ecollent™ GPB | Lucent Polymers, Inc. | PBT | Ecollent™ |
| POCAN® KU 2-7317 000000 | LANXESS GmbH | PBT | POCAN® |
| Durethan® B 35 FA 000000 | LANXESS Corporation | Nylon 6 | Durethan® |