Kynar Flex® 2800-20
| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | Arkema |
| Trademark: | Kynar Flex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Utg7mb_Kynar-Flex-2800-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KYNAR FLEX® 2800-20 is a pelletized, semi-crystalline VF 2 based copolymer. KYNAR FLEX® 2800-20 has been specifically designed for applications requiring high flexibility and improved resistance to impact. KYNAR FLEX® 2800-20 can be extruded or injection molded. ADVANTAGES: Improved flexibility at subzero temperatures to -20°C(-4°F) Improved stress crack resistance to high pH solutions Improved elongation at break ADDITIONAL CHARACTERISTICS: Easy processability using conventional equipment Excellent thermal stability Retains properties after aging Pigmentable UL temperature rating 125°C Radiation crosslinking |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.77 to 1.80 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 60 to 70 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 20.0 to 34.5 | MPa | |
| Break, 23°C | 17.2 to 34.5 | MPa | |
| Tensile Elongation (Break, 23°C) | 100 to 300 | % | ASTM D638 |
| Flexural Modulus (23°C) | 483 to 758 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 20.7 to 34.5 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 31.0 to 41.4 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 140 to 145 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 1(20°C) | 2.0E+14 | ohms·cm | ASTM D257 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (232°C, 100 sec^-1) | 1200 to 2000 | Pa·s | ASTM D3835 |
| Note Message | |
|---|---|
| 1 . | 65% R.H. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ad-Tech Polyester NO. 38 | Ad-Tech Plastic Systems Corp. | Polyester, TS | Ad-Tech Polyester |
| CALP WS641 | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| LEXAN™ BY2710X resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| LNP™ LUBRICOMP™ RL0039XP compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |
| PALMID® R 66 S GF 20 | pal plast GmbH | Nylon 66 | PALMID® |