MAJORIS G200
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UpUvQt_MAJORIS-G200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJORIS G200 is a special long glass fibre reinforced polypropylene grade, for injection moulding and extrusion. The long glass fibres, chemically coupled to the polypropylene matrix, are providing with outstanding mechanical properties. MAJORIS G200 is available both in natural (MAJORIS G200) and black (MAJORIS G200 - 8229). Other colours can be provided on request. APPLICATIONS MAJORIS G200 is intended for injection moulding of highly demanding technical applications. The excellent properties of MAJORIS G200 make it suitable for:
MAJORIS G200 can, in many of these applications, substitute other engineering plastics or metal alloys. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 80.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus | 4600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 13 | kJ/m² | ISO 179/1eA |
| 23°C | 10 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 159 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 142 | °C | ISO 306/B |
| CLTE - Flow | ASTM D696 | ||
| -30°C | 5.9E-5 | cm/cm/°C | ASTM D696 |
| 23°C | 5.4E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 230 - 250 | °C | |
| Processing (Melt) Temp | 250 - 280 | °C | |
| Mold Temperature | 80.0 - 100 | °C | |
| Injection Pressure | 30.0 - 60.0 | MPa | |
| Injection Rate | Slow | ||
| Screw Speed | 30 - 150 | rpm | |
| Injection Velocity | 20 - 30 | mm/sec |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressureBack pressure: as low as possible, 0 to 10% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2925-75 Clear 8392 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| YUPLENE® B351F | SK Global Chemical | PP Impact Copolymer | YUPLENE® |
| Calprene® 401 | Dynasol Elastomers | SBS | Calprene® |
| CALIBRE™ IM 401-11 | Trinseo | PC | CALIBRE™ |
| Hostacom TRC 411Y C11543 | LyondellBasell Industries | PP Copolymer | Hostacom |