KOCETAL® CF702
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Kolon Plastics, Inc. |
| Trademark: | KOCETAL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UpGEcG_KOCETAL-CF702.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Kocetal CF702 is carbon fiber reinforced grade for high stiffness and electrical conductivity. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.90 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 60%RH) | 0.22 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 87 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 80.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 4.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 6600 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 47 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 164 | °C | |
| 1.8 MPa, Unannealed | 160 | °C | |
| Melting Temperature | 166 | °C | |
| CLTE - Flow | 6.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+7 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+6 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Regrind | 30 | % | |
| Rear Temperature | 170 to 190 | °C | |
| Middle Temperature | 190 to 210 | °C | |
| Front Temperature | 200 to 220 | °C | |
| Nozzle Temperature | 200 to 220 | °C | |
| Processing (Melt) Temp | 165 to 220 | °C | |
| Mold Temperature | 70.0 to 120 | °C | |
| Injection Pressure | 68.6 to 118 | MPa | |
| Holding Pressure | 98.1 | MPa | |
| Back Pressure | 1.96 to 4.90 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ E111G | Prime Polymer Co., Ltd. | PP Homopolymer | Prime Polypro™ |
| ELASTOSIL® RT 563 | Wacker Chemie AG | Silicone | ELASTOSIL® RT |
| Hanwha Total PP BJ522 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Impact Copolymer | Hanwha Total PP |
| INNOPOL® PP CS 2-3522 TO BU | Inno-Comp Ltd. | PP Copolymer | INNOPOL® PP |
| ALTECH® PC ECO 1000/578 | ALBIS PLASTIC GmbH | PC | ALTECH® PC |