VALOX™ 7062 resin
| Category: | PBT+PET , Polybutylene Terephthalate + PET |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UpGBqX_VALOX-7062-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VALOX 7062 is Mineral filled PBT injection molding grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.81 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (265°C/1.2 kg) | 21.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 1.2 to 1.9 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 140 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 60.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 3900 | MPa | ISO 178 |
| Flexural Stress | 100 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 74.0 | mg | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C 2 | 2.0 | kJ/m² | |
| 23°C 3 | 2.0 | kJ/m² | |
| Notched Izod Impact | |||
| -30°C | 3.0 | J/m | ASTM D256 |
| 23°C | 3.0 | J/m | ASTM D256 |
| -30°C 4 | 3.0 | kJ/m² | ISO 180/1A |
| 23°C 5 | 3.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 65.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 175 | °C | ASTM D1525, ISO 306/B50, ISO 306/B120 6 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 80°C | 9.0E-5 | cm/cm/°C | |
| Transverse : 23 to 80°C | 9.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 3.70 | ||
| 60 Hz | 3.70 | ||
| 1 MHz | 3.60 | ||
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 2.0E-3 | ||
| 60 Hz | 2.0E-3 | ||
| 1 MHz | 0.015 | ||
| Comparative Tracking Index | 475 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Glow Wire Flammability Index (3.20 mm) | 650 | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*3 sp=62mm |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| 6 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| megol® P08 A60X3 | API SpA | SEBS | megol® |
| NEXUS PP HPP50 | Nexus Resin Group, LLC. | PP Homopolymer | NEXUS PP |
| EGYPTENE HD 5218 EA | Sidpec (Sidi Kerir Petrochemicals Co.) | HDPE | EGYPTENE |
| Piolen® PS GK30A15 | PiO Kunststoffe GmbH & Co KG | PP Copolymer | Piolen® PS |
| LEXAN™ FST9405 resin | SABIC Innovative Plastics | PC | LEXAN™ |