SUMIKAEXCEL® PES 3601GL20
| Category: | PESU , Polyethersulfone |
| Manufacturer: | Sumitomo Chemical Co., Ltd. |
| Trademark: | SUMIKAEXCEL® PES |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UoZMcs_SUMIKAEXCEL-PES-3601GL20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SUMIKAEXCEL® PES 3601GL20 is a Polyethersulfone (PESU) material filled with 20% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of SUMIKAEXCEL® PES 3601GL20 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.30 | % | |
| Across Flow | 0.40 | % | |
| Water Absorption (24 hr) | 0.36 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 134 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 124 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 5900 | MPa | ASTM D790 |
| Flexural Strength | 172 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.40 mm) | 80 | J/m | ASTM D256 |
| Unnotched Izod Impact (6.40 mm) | 430 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 210 | °C | ASTM D648 |
| CLTE | ASTM D696 | ||
| Flow : -50 to 150°C | 2.6E-5 | cm/cm/°C | |
| Transverse : 50 to 150°C | 4.8E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Arc Resistance | 150 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.430 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 310 to 340 | °C | |
| Middle Temperature | 340 to 380 | °C | |
| Front Temperature | 340 to 380 | °C | |
| Nozzle Temperature | 340 to 380 | °C | |
| Processing (Melt) Temp | 350 to 360 | °C | |
| Mold Temperature | 120 to 160 | °C | |
| Injection Pressure | 118 to 157 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 58.4 to 78.4 | MPa | |
| Back Pressure | 4.90 to 9.80 | MPa | |
| Screw Speed | 30 to 50 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4082 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| SABIC® PP QR678K | Saudi Basic Industries Corporation (SABIC) | PP Random Copolymer | SABIC® PP |
| THERMOLAST® K TP5CDZ (Series: EX) | KRAIBURG TPE | TPE | THERMOLAST® K |
| WELLAMID Nylon 6000 GV 35 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Ultramid® B3WG6 GP | BASF Corporation | Nylon 6 | Ultramid® |