Rilsan® BZM 30 O TLDA
| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Umga1v_Rilsan-BZM-30-O-TLDA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan ® BZM 30 O TLDA is a fibreglass reinforced polyamide 11 produced from a renewable source. This natural grade dedicated to injection is specially designed for drinking water applications: ACS (France), WRAS (UK), NSF61 (USA), KTW and DVGW/W270 (Germany). MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (235°C/5.0 kg) | 9.00 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 81 | ||
| Shore D, 15 sec | 77 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6800 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 122 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 9.0 | % | ISO 527-2 |
| Flexural Modulus | 5500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 18 | kJ/m² | |
| 23°C | 26 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 189 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ISO Shortname | PA11, MHLR, 18-070, GF 30 | ISO 1874 | |
| Renewable Carbon Conent | > 97 | % | ASTM D6866 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 250 to 290 | °C | |
| Mold Temperature | 40.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT5100-00 | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| WPP PP PPH4TF4-Black | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| ExxonMobil™ PP3295G1 | ExxonMobil Chemical | PP Homopolymer | ExxonMobil™ |
| Karina NATURAL PVC COMPOUND 900-25/ 1-AYR-IS-LMP (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| CYCOLOY™ XCY620S resin | SABIC Innovative Plastics | PC+ABS | CYCOLOY™ |