TOTAL Polyethylene Lumicene® M 6040
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UlHLLv_TOTAL-Polyethylene-Lumicene-M-6040.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lumicene® mPE M 6040 is a second generation metallocene high density Polyethylene. Lumicene® mPE M 6040 can be processed at high output rates with low extrusion pressure, low neck-in, excellent drawability and gauge control in comparison with conventional LLDPE and first generation metallocene based polyethylene. The high stiffness combined with good optical properties brings a significant down-gauging potential. Lumicene® mPE M 6040 is a versatile resin that can be used in pure or in blend for the production of both monolayer and multilayer film. Typical applications are: specialty film, hygiene film, embossed film, compounds and consumer and automatic packaging, such as produce bags, mailing and hygiene overwrap film. The high density of Lumicene® mPE M 6040 enables its use in applications with moisture barrier requirements, such as dry food packaging, and brings improved heat resistance, compared to commonly used HDPE. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 20 µm, cast film | 23.0 | MPa | ISO 527-3 |
| TD : Yield, 20 µm, cast film | 24.0 | MPa | ISO 527-3 |
| MD : Fracture, 20 µm, cast film | 26.0 | MPa | ISO 527-3 |
| TD : Fracture, 20 µm, cast film | 34.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Fracture, 20 µm, cast film | 520 | % | ISO 527-3 |
| TD : Fracture, 20 µm, cast film | 850 | % | ISO 527-3 |
| Dart Drop Impact (20 µm, Cast Film) | 40 | g | ISO 7765-1 |
| Elmendorf Tear Strength 1 | ISO 6383-2 | ||
| MD : 20.0 µm | 8.0 | kN/m | ISO 6383-2 |
| TD : 20.0 µm | 70.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 132 | °C | ISO 306 |
| Melting Temperature | 134 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 20.0 µm, Cast Film) | 51 | ASTM D2457 | |
| Haze (20.0 µm, Cast Film) | 12 | % | ISO 14782 |
| Additional Information |
|---|
| Laboratory test specimens produced at the following extrusion conditions: die gap = 250 µm, chill roll temperature = 20°C, throughput = 7 kg/h, melt temperature = 260 °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 220 - 280 | °C | |
| Take-Off Roll | 20.0 - 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Cast Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RJM EL701 | RJM International, Inc. | PP, Unspecified | RJM |
| Shuman PS 881 | Shuman Plastics, Inc. | PS (MIPS) | Shuman PS |
| NORYL GTX鈩?GTX679 resin | SABIC Innovative Plastics | PPE+PS+Nylon | NORYL GTX™ |
| HiFill® PA6/6 LGF60 HS L UV 12mm | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Jiangsu Sinarise ZM70 | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |