KF 1300
| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | Kureha Corporation |
| Trademark: | KF |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UlBuyr_KF-1300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| KF 1300 PVDF homopolymer is a high viscosity PVDF resin typically processed by extrusion or compression molding. This material offers excellent chemical resistance at ambient and elevated temperatures. PVDF is also inherently UV stable, mechanically tough, abrasion |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.77 to 1.79 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 230°C/21.6 kg | 11 | g/10 min | |
| 230°C/5.0 kg | 0.80 to 1.4 | g/10 min | |
| Water Absorption (Equilibrium) | 0.030 | % | ASTM D570 |
| Solution Viscosity - DMF (30°C) | 130 | cm³/g |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness 1(Shore D, 23°C) | 78 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2580 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 67.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 25 | % | ISO 527-2 |
| Flexural Modulus | 1870 | MPa | ISO 178 |
| Flexural Stress | 70.0 | MPa | ISO 178 |
| Compressive Modulus | 2020 | MPa | ISO 604 |
| Compressive Stress | 68.0 | MPa | ISO 604 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g) | 31.0 | mg | ISO 9352 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Area) | ASTM D256 | ||
| -40°C | 3.60 | kJ/m² | |
| -20°C | 11.5 | kJ/m² | |
| 0°C | 37.0 | kJ/m² | |
| 20°C | 77.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -47.0 | °C | ASTM D746 |
| Glass Transition Temperature | -35.0 | °C | DMA |
| Vicat Softening Temperature | 173 | °C | ISO 306/A50 |
| Peak Melting Temperature | 173 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 140 | °C | ASTM D3418 |
| CLTE - Flow (23 to 80°C) | 1.6E-4 | cm/cm/°C | ISO 11359-2 |
| Specific Heat (23°C) | 1200 | J/kg/°C | JIS K7123 |
| Thermal Conductivity (23°C) | 0.17 | W/m/K | ASTM E1530 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+14 to 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (0.0340 mm) | 300 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 10.0 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 0.015 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 | |
| Oxygen Index 2 | 44 | % | ISO 4589-2 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Refractive Index 3 | 1.420 | ASTM D542 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity | ASTM D3835 | ||
| 240°C, 50.0 sec^-1 | 5000 | Pa·s | |
| 260°C, 50.0 sec^-1 | 4500 | Pa·s |
| Note Message | |
|---|---|
| 1 . | 50N |
| 2 . | Type-IV |
| 3 . | 25°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 199 X 106955 | RTP Company | PP, Unspecified | RTP |
| Xuchuan XCRH-30 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Karina WHITE PVC COMPOUND 851-10/1-E-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1850-8322 | Lehmann & Voss & Co. | PBT | LUVOCOM® |
| Braskem PE LDF2023 | Braskem IDESA | LDPE | Braskem PE |