HiFill® PA6/6 IM HS L BK
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UkxGLx_HiFill-PA6-6-IM-HS-L-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HiFill® PA6/6 IM HS L BK is a Polyamide 66 (Nylon 66) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.6 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.3 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 48.3 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 48 | % | ASTM D638 |
| Flexural Modulus | 1790 | MPa | ASTM D790 |
| Flexural Strength | 59.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.18 mm | 180 | J/m | |
| 23°C, 3.18 mm | 800 | J/m | |
| Unnotched Izod Impact (3.18 mm) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 216 | °C | |
| 1.8 MPa, Unannealed | 71.1 | °C | |
| CLTE - Flow | 7.9E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 17 | kV/mm | ASTM D149 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 2.0 to 4.0 | % | |
| Rear Temperature | 266 to 304 | °C | |
| Middle Temperature | 266 to 304 | °C | |
| Front Temperature | 266 to 304 | °C | |
| Processing (Melt) Temp | 260 to 282 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BT36 ST | A. Schulman Europe | Nylon 6 | VITAMIDE® |
| Borlink™ LE0500 | Borealis AG | PE, Unspecified | Borlink™ |
| CGPC PVC H-80 | China General Plastics Corporation | PVC, Unspecified | CGPC PVC |
| IDI BMC B20 (Glass Content 8%) | IDI Composites International | TS, Unspecified | IDI BMC |
| LNP™ THERMOCOMP™ EF006H compound | SABIC Innovative Plastics | PEI | LNP™ THERMOCOMP™ |