TOTAL Polyethylene MDPE HF 513
| Category: | MDPE , Medium Density Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ukm2Rg_TOTAL-Polyethylene-MDPE-HF-513.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MDPE HF 513 is a medium density polyethylene produced by slurry loop low pressure process with hexene as co-monomer. MDPE HF 513 is a semi-high molecular weight polyethylene giving excellent mechanical properties. It shows a broad molecular weight distribution ensuring outstanding processability. MDPE HF 513 can be used alone, blended or coextruded in a wide variety of blown film applications : consumer, industrial, food or hygiene packaging. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.934 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.15 | g/10 min | ISO 1133 |
| 190°C/21.6 kg | 15 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 620 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 20 µm, blown film | 20.0 | MPa | ISO 527-3 |
| TD : Yield, 20 µm, blown film | 19.0 | MPa | ISO 527-3 |
| MD : Yield, 40 µm, blown film | 18.0 | MPa | ISO 527-3 |
| TD : Yield, 40 µm, blown film | 18.0 | MPa | ISO 527-3 |
| MD : Broken, 20 µm, blown film | 65.0 | MPa | ISO 527-3 |
| TD : Broken, 20 µm, blown film | 52.0 | MPa | ISO 527-3 |
| MD : Broken, 40 µm, blown film | 55.0 | MPa | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 52.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 20 µm, blown film | 400 | % | ISO 527-3 |
| TD : Broken, 20 µm, blown film | 500 | % | ISO 527-3 |
| MD : Broken, 40 µm, blown film | 540 | % | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 620 | % | ISO 527-3 |
| Dart Drop Impact | ISO 7765-1 | ||
| 20 µm, blown film | 220 | g | ISO 7765-1 |
| 40 µm, blown film | 290 | g | ISO 7765-1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 118 | °C | ISO 306 |
| Melting Temperature (DSC) | 125 | °C | ISO 3146 |
| Additional Information |
|---|
| Elmendorf, ISO 6383-2, MD, Blown Film, 20 µm: 11 N/mmElmendorf, ISO 6383-2, TD, Blown Film, 20 µm: 135 N/mmElmendorf, ISO 6383-2, MD, Blown Film, 40 µm: 24 N/mmElmendorf, ISO 6383-2, TD, Blown Film, 40 µm: 185 N/mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 190 - 220 | °C | |
| Cylinder Zone 2 Temp. | 190 - 220 | °C | |
| Cylinder Zone 3 Temp. | 190 - 220 | °C | |
| Cylinder Zone 4 Temp. | 190 - 220 | °C | |
| Cylinder Zone 5 Temp. | 190 - 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermylene® P4-9900-0520 | Asahi Kasei Plastics North America Inc. | PP, Unspecified | Thermylene® |
| Nanjing Hongrui PBT T1304 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PBT | Nanjing Hongrui PBT |
| NEXUS Reprocessed Nylon 66 G33 RBK | Nexus Resin Group, LLC. | Nylon 66 | NEXUS Reprocessed |
| Ferro PP TPP40AC35WH | Ferro Corporation | PP Homopolymer | Ferro PP |
| Sylvin 4200-88UV Clear Blue 8488 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |