Arlatex® 1372R
| Category: | SBR, Emulsion , Emulsion Styrene Butadiene Rubber |
| Manufacturer: | INSA |
| Trademark: | Arlatex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UkGosq_Arlatex-1372R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: A1372R an aqueous dispersion of a carboxylated styrene-butadiene copolymer manufactured by polymerization in emulsion. Applications: A1372R is a product specially designed to be employed as backing in carpets and rugs with any type of fabric. It can be applied on canoe systems (simple or double) or by direct application. As a base to formulate backings, adhesives, textile pressings or in applications with no-fabrics. It can be applied in foam. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Antioxidant Additive | Non Staining | ||
| pH (25°C) | 9.0 to 9.4 | Internal Method | |
| Solids Content | 52 to 53 | % | Internal Method |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brookfield Viscosity - LVT #2, 30 rpm | < 500 | mPa·s | Internal Method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emulsifier | Anionic | ||
| Mechanical Stability - Osther OH Beach @ 15000 rpm | 30.0 | min | Internal Method |
| Temperature - Vitreous Transition | 0.00 | °C | DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene G40P100-04UV | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| Nylfor® R 6 CA/20 E3 EV GREY 7102/1 | SO.F.TER. SPA | Nylon 6 | Nylfor® |
| NYLOY® KF-0010N 6121W | Nytex Composites Co., Ltd. | Nylon, Unspecified | NYLOY® |
| FRAGOM LC/125 RR | Crosspolimeri S.p.A. | Polyolefin, Unspecified | FRAGOM |
| Karina IVORY PVC COMPOUND 807D35/1-C-AC-HSF | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |