Lucet® N145-LD
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lucet® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UhuFK4_Lucet-N145-LD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lucet® N145-LD is an Acetal (POM) Copolymer material. It is available in North America for injection molding. Important attributes of Lucet® N145-LD are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 45 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.8 to 2.1 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.22 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 82 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 59.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 45 | % | ASTM D638 |
| Flexural Modulus | 2550 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 93.1 | MPa | ASTM D790 |
| Coefficient of Friction (vs. Itself - Static) | 0.16 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 44 | J/m | |
| 23°C | 54 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 160 | °C | |
| 1.8 MPa, Unannealed | 110 | °C | |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 24 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.80 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 7.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.794 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Rear Temperature | 160 to 180 | °C | |
| Middle Temperature | 180 to 200 | °C | |
| Front Temperature | 190 to 200 | °C | |
| Nozzle Temperature | 190 to 210 | °C | |
| Processing (Melt) Temp | 190 to 200 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 39.2 to 68.6 | MPa | |
| Back Pressure | 3.92 to 7.84 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TechnoMid B330 | TechnoCompound GmbH | Nylon 6 | TechnoMid |
| Ultraform® N 2650 Z2 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| COPYLENE® CR020CL | Phillips 66 | PP Random Copolymer | COPYLENE® |
| Karina IVORY PVC COMPOUND 105900-35/1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plaskon 3400-2 | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |