PULSE™ EXT 100
| Category: | PC+ABS , PC/ABS Engineering Resin |
| Manufacturer: | Trinseo |
| Trademark: | PULSE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UgySD7_PULSE-EXT-100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PULSE EXT 100 engineering resin has been designed to provide excellent processability, high heat resistance, and high impact strength at both room and low temperatures. PULSE EXT 100 engineering resin has been used in automotive exterior trim applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.14 | g/cm³ | ASTM D792 |
| -- | 1140 | kg/m³ | ISO 1183 1 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 1.3 | g/10 min | ASTM D1238 |
| Melt volume-flow rate (265°C/5.0 kg) | 10.0 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage - Flow | 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile modulus | 2100 | MPa | ISO 527-2 3 |
| Tensile Strength | |||
| Yield 4 | 51.7 | MPa | ASTM D638 |
| Yield | 54.0 | MPa | ISO 527-2 5 |
| Tensile Strain | |||
| Yield | 4.8 | % | ISO 527-2 6 |
| Break 7 | 80 | % | ASTM D638 |
| Nominal strain at break | > 50 | % | ISO 527-2 8 |
| Flexural Modulus | 2240 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy notched impact strength | ISO 179/1eA 9 | ||
| -30°C | 24.0 | kJ/m² | |
| 23°C | 61.0 | kJ/m² | |
| Charpy impact strength | ISO 179/1eU 10 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact 11 | ASTM D256 | ||
| -29°C, 3.20 mm | 480 | J/m | |
| 23°C, 3.20 mm | 640 | J/m | |
| Instrumented Dart Impact 12 | ASTM D3763 | ||
| -29°C, 3.20 mm, Total Energy | 59.9 | J | |
| 23°C, 3.20 mm, Total Energy | 54.2 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 124 | °C | ASTM D648 |
| 0.45 MPa | 134 | °C | ISO 75-2 13 |
| 1.8 MPa, Unannealed, 3.20 mm | 107 | °C | ASTM D648 |
| 1.8 MPa | 111 | °C | ISO 75-2 14 |
| Vicat Softening Temperature (50°C/h, B (50N)) | 133 | °C | ISO 306 15 |
| CLTE - Flow | |||
| -40 to 82°C | 7.2E-5 | cm/cm/°C | ASTM D696 |
| -- | 7.2E-5 | cm/cm/°C | ISO 11359-2 16 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Density | 1.02 | g/cm³ | |
| Melt Specific Heat | 1980 | J/kg/°C | ASTM C351 |
| Melt Thermal Conductivity | 0.26 | W/m/K | ASTM C177 |
| No Flow Temperature | 160 | °C | |
| Ejection Temperature | 138 | °C |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Type I, 51 mm/min |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Type I, 51 mm/min |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | 0.25 mm Notch Depth |
| 12 . | 3.39 m/sec |
| 13 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 14 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 15 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 16 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3890 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Sylvin 86025-38DUV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| APICAL 50NP | Kaneka North America LLC | Film, PI | APICAL |
| Romiloy® 1045 F PG | ROMIRA GmbH | PC+ABS | Romiloy® |
| OTECH PVC OE7533 - Calendering | OTECH Corporation | PVC, Unspecified | OTECH PVC |