| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | RheTech, Inc. |
| Trademark: | RheTech Polypropylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UgxI7R_RheTech-Polypropylene-P254-00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene Copolymer, Natural. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.898 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 64 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 24.1 | MPa | ASTM D638 |
| Flexural Modulus | 1070 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 120 | J/m | ASTM D256 |
| Dart Drop Impact | 21.5 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 91.1 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 57.2 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 - 82.2 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 188 - 216 | °C | |
| Middle Temperature | 193 - 221 | °C | |
| Front Temperature | 199 - 227 | °C | |
| Nozzle Temperature | 204 - 216 | °C | |
| Mold Temperature | 26.7 - 48.9 | °C | |
| Injection Pressure | 2.76 - 10.3 | MPa | |
| Holding Pressure | 2.07 - 8.27 | MPa | |
| Back Pressure | 0.345 - 1.03 | MPa |
| Injection instructions |
|---|
| Injection Speed: Variable - Application DependantScrew RPM: Recovery 3 seconds before mold opensCycle Time: Wall Thickness Dependant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Salflex 810CI | Salflex Polymers Ltd. | PP Copolymer | Salflex |
| Sasol Polymers PP HNR101 | Sasol Polymers | PP Homopolymer | Sasol Polymers PP |
| SLOVAMID® 6 GF 20 FRA 5 | Plastcom | Nylon 6 | SLOVAMID® 6 |
| NORYL™ HM4025H resin | SABIC Innovative Plastics Asia Pacific | PPE+PS | NORYL™ |
| 3M™ Dyneon™ TFM™ Modified PTFE TFM 2070Z | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE |