OXPEKK® IG230C
| Category: | PEKK , Polyetherketoneketone |
| Manufacturer: | Oxford Performance Materials, Inc. |
| Trademark: | OXPEKK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UgmgUA_OXPEKK-IG230C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
OXPEKK® IG230C is a Polyetherketoneketone (PEKK) material filled with 30% carbon fiber. It is available in Europe or North America. Typical application of OXPEKK® IG230C: Medical/Healthcare |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 | % | ASTM D955 |
| Water Absorption (24 hr) | < 0.030 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ASTM D638 |
| Tensile Strength (Break) | 262 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 | % | ASTM D638 |
| Flexural Modulus | 2200 | MPa | ASTM D790 |
| Flexural Strength | 291 | MPa | ASTM D790 |
| Compressive Strength | 241 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 321 | °C | ASTM D648 |
| Glass Transition Temperature | 163 | °C | DSC |
| Melting Temperature | 360 | °C | DSC |
| CLTE - Flow | 1.0E-5 | cm/cm/°C | ASTM D696 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ResMart Ultra HDPE 20 | ResMart | HDPE | ResMart Ultra |
| RTP 103 White | RTP Company | PP, Unspecified | RTP |
| 4PET® 9L22130 HL | 4Plas | PET | 4PET® |
| KYOCERA KE-870 | KYOCERA Chemical Corporation | Epoxy | KYOCERA |
| Wanthane® WHT-1495B | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |