SLOVAMID® 66 GF 30 SLS
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Plastcom |
| Trademark: | SLOVAMID® 66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UgXB2a_SLOVAMID-66-GF-30-SLS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Chemically reinforced with 30 % glass fibre and with molybdenium disulphide, suitable for mouldings with high strength and toughness and for products for better slide propperties. Used in the automotive, engineering and electrical industry. Delivered in black colour or natural. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | STM 64 0808 | ||
| Across Flow | 0.90 | % | |
| Flow | 0.70 | % | |
| Water Content | 0.20 | % | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9500 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 165 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 8700 | MPa | ISO 178 |
| Flexural Stress | 240 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 11 | kJ/m² | |
| 23°C | 14 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 75 | kJ/m² | |
| 23°C | 75 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 250 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 250 | °C | ISO 306/B |
| Melting Temperature (DSC) | 262 | °C | ISO 3146 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 70.0 to 100 | °C | |
| Injection Pressure | 70.0 to 120 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Scolefin 52 G 13-0 | Ravago Group | PP Homopolymer | Scolefin |
| THERMOLAST® K TF5STE (Series: FC/CS) | KRAIBURG TPE | TPE | THERMOLAST® K |
| ALCOM® PA6 900/1 GF15 MR25 | ALBIS PLASTIC GmbH | Nylon 6 | ALCOM® PA6 |
| HiFill® XMD POM 0167 LE | Techmer Engineered Solutions | Acetal (POM) Copolymer | HiFill® |
| Karina IVORY PVC COMPOUND BTR-700D35/ 1-B-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |