| PA 6 for injection moulding, chemically strengthened with 65% of glass fibre, for mouldings with high strength and toughness used in the automotive, electrical, engineering and consumer-goods industry. Application: grips of electrotools, hobby tools, gears, covers of electric appliances, cooling skrews of blowers, electromotors, carrying parts in the automotive industry. Replacement of metal parts from ZAMAC and etc.Delivered in natural mode and in black. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.71 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | STM 64 0808 | ||
| Across Flow | 0.30 | % | |
| Flow | 0.20 | % | |
| Water Content | 0.10 | % | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 22800 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 270 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 2.3 | % | ISO 527-2 |
| Flexural Modulus | 18300 | MPa | ISO 178 |
| Flexural Stress | 420 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 18 | kJ/m² | |
| 23°C | 26 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 95 | kJ/m² | |
| 23°C | 100 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 218 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 222 | °C | ISO 306/B |
| Melting Temperature (DSC) | 222 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 6.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength | 33 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 270 to 300 | °C | |
| Mold Temperature | 90.0 to 100 | °C | |
| Injection Pressure | 90.0 to 150 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 203 C TFE 20 | RTP Company | Nylon 11 | RTP |
| Sylvin 2944-91 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Monprene® OM-10165 | Teknor Apex Company | TPE | Monprene® |
| Petrothene® NA362 | LyondellBasell Industries | LDPE | Petrothene® |
| Durethan® BG 30 X H2.0 XF 901510 | LANXESS GmbH | Nylon 6 | Durethan® |