RTP 200C TFE 20
| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UfvlUZ_RTP-200C-TFE-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.1 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 108 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1380 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 48.3 | MPa | ASTM D638 |
| -- | 48.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 6.0 | % | ASTM D638 |
| Flexural Modulus | 1240 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| -- | 82.7 | MPa | ASTM D790 |
| Yield | 82.7 | MPa | ASTM D790 |
| Compressive Strength | 68.9 | MPa | ASTM D695 |
| Coefficient of Friction (With Metal-Dynamic) | 0.15 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 75 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 480 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 154 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 60.0 | °C | ASTM D648 |
| CLTE - Flow | 8.8E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.35 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength | 18 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.20 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.10 | ASTM D150 | |
| Arc Resistance | 100 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm, RTP Tested) | HB | UL 94 |
| Additional Information |
|---|
| Molding shrinkage, Linear-flow, ASTM D955, 0.25in: 15mil/inWear factor, K, ASTM D648: 25E-10in³min/ft/lb/hrThe coefficient of friction was tested on a Falex Model No.6 Wear Testing Machine at 50 FPM, 2000 PV, against C1018 steel of hardness 15-25 Rockwell C, 14-17 micro smoothness. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 218 - 274 | °C | |
| Middle Temperature | 218 - 274 | °C | |
| Front Temperature | 218 - 274 | °C | |
| Mold Temperature | 37.8 - 65.6 | °C | |
| Injection Pressure | 68.9 - 103 | MPa | |
| Back Pressure | 0.172 - 0.345 | MPa | |
| Screw Speed | 50 - 90 | rpm | |
| Clamp Tonnage | 6.9 - 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CERTENE™ LLBF-120F | Muehlstein | LLDPE | CERTENE™ |
| Daelim Po1y® LH-144 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| Hifax RTA3223 | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |
| Kingfa PP-V16 | Kingfa | PP, Unspecified | Kingfa |
| Sylvin 6244-42D Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |