PRE-ELEC® PC 1431
| Category: | PC , Polycarbonate |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Uf00h8_PRE-ELEC-PC-1431.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® PC 1431 is a conductive thermoplastic compound based on polycarbonate. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity. PRE-ELEC® PC 1431 has excellent mechanical properties and is easy to injection mould. Typical applications include technical parts requiring good impact strength, higher rigidity and very good temperature resistance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.25 | g/cm³ | ASTM D792 |
| -- | 1.24 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 300°C/1.2 kg | 4.0 | g/10 min | |
| 300°C/2.16 kg | 10 | g/10 min | |
| Molding Shrinkage - Flow | 0.60 | % | ASTM D955, ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 85 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Across Flow : Yield | 44.8 | MPa | ASTM D638 |
| Flow : Yield | 50.3 | MPa | ASTM D638 |
| Across Flow : Yield | 45.0 | MPa | ISO 527-2 |
| Flow : Yield | 50.0 | MPa | ISO 527-2 |
| Across Flow | 44.1 | MPa | ASTM D638 |
| Flow | 46.9 | MPa | ASTM D638 |
| -- 1 | 44.0 | MPa | ISO 527-2 |
| 0.400 mm 2 | 47.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Across Flow : Yield | 6.0 | % | |
| Flow : Yield | 6.0 | % | |
| Break, 0.400 mm 3 | 15 | % | |
| Break, 0.400 mm 4 | 20 | % | |
| Flexural Modulus | |||
| 4.00 mm | 2480 | MPa | ASTM D790 |
| 4.00 mm | 2500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 5 | |||
| -20°C | 15 | kJ/m² | ASTM D256 |
| -20°C | 16 | kJ/m² | ISO 179 |
| 23°C | 22 | kJ/m² | ISO 179 |
| 23°C | 21 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength 6 | |||
| -20°C | No Break | ASTM D256, ISO 179 | |
| 23°C | No Break | ISO 179, ASTM D256 | |
| Notched Izod Impact (Area) | ASTM D256 | ||
| -20°C, 4.00 mm | 14.7 | kJ/m² | |
| 23°C, 4.00 mm | 21.0 | kJ/m² | |
| Notched Izod Impact Strength 7 | ISO 180 | ||
| -20°C | 14 | kJ/m² | |
| 23°C | 20 | kJ/m² | |
| Unnotched Izod Impact (Area) | ASTM D256 | ||
| -20°C, 4.00 mm | No Break | ||
| 23°C, 4.00 mm | No Break | ||
| Unnotched Izod Impact Strength 8 | ISO 180 | ||
| -20°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 138 | °C | ASTM D648B, ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 125 | °C | ASTM D648A, ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 147 | °C | ASTM D1525, ISO 306/A50 6 9 |
| -- | 140 | °C | ASTM D1525, ISO 306/B50 7 10 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+6 | ohms | IEC 61340-2-3 |
| Volume Resistivity | < 1.0E+4 | ohms·cm | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 90.0 to 110 | °C | |
| Injection Pressure | 100 to 152 | MPa | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | .4 mm Thickness, Across Flow |
| 2 . | Flow |
| 3 . | Across Flow |
| 4 . | Flow |
| 5 . | 4 mm thickness |
| 6 . | 4 mm thickness |
| 7 . | 4 mm thickness |
| 8 . | 4 mm thickness |
| 9 . | Rate A (50°C/h), Loading 2 (50 N) |
| 10 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumitomo Phenolic FM 4005X4649 | Sumitomo Bakelite North America, Inc. | Phenolic | Sumitomo Phenolic |
| TARFLON™ SC-300 | Idemitsu Kosan Co., Ltd. | PC+PET | TARFLON™ |
| Nypol® PA B3 G15 HL TZ PRTA010 NT333 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| Nylene® 6111 HS | Custom Resins Group | Nylon 66 | Nylene® |
| Epoxies, Ect. 20-1715 | Epoxies, Etc. | Silicone Gel | Epoxies, Ect. |