Multilon® TN-3616Q
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | TEIJIN LIMITED |
| Trademark: | Multilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UeM3vW_Multilon-TN-3616Q.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC/ABS polymer alloy |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 4.00 mm | 0.50 to 0.70 | % | |
| Flow : 4.00 mm | 0.50 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1760 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 45.0 | MPa | |
| Break | 45.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 3.0 | % | |
| Break | 120 | % | |
| Flexural Modulus 1 | 1800 | MPa | ISO 178 |
| Flexural Stress 2 | 74.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 55 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 112 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 97.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 112 | °C | ISO 306/B50 |
| CLTE | ISO 11359-2 | ||
| Flow | 8.0E-5 | cm/cm/°C | |
| Transverse | 8.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 to 1.0E+11 | ohms | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RABALON® MJ4300C | Mitsubishi Chemical Performance Polymers, Inc. | TPE | RABALON® |
| Titacon® ST220 | Titan Plastics Compounds Co., Ltd. | Acetal (POM) Copolymer | Titacon® |
| XYLEX™ X8303 resin | SABIC Innovative Plastics Europe | PC+Polyester | XYLEX™ |
| Niche PA66GF33BK | Niche Polymer, LLC | Nylon 66 | Niche |
| Elastron® V P.V101.A30.N | Elastron USA, Inc. | TPV | Elastron® V |