Sipolprene® 46185
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | SIPOL S.p.A |
| Trademark: | Sipolprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ue76wG_Sipolprene-46185.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sipolprene® 46185 is an ether ester thermoplastic elastomer (TPC-ET), developed and manufactured by Sipol, with a nominal hardness of Shore D 44, a low modulus, and a rheological behaviour, which makes it suitable for injection molding and extrusion processing. Sipolprene® 46185 comes in a natural color with a standard stabilisation package, fully in compliance with American FDA and European EU 10/2011 Food Contact Regulations. Black color and/or UV stabilised and/or heat stabilised are all available in dry blend version on request. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 34 | g/10 min | ASTM D1238, ISO 1133 |
| Water Absorption (23°C, 24 hr) | 0.45 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 44 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 34.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 700 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 80.0 | MPa | ASTM D790, ISO 178 |
| Abrasion Resistance | 19.0 | mm³ | DIN 53516 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 142 | kN/m | ASTM D1004 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 149 | °C | ISO 306/A50, ASTM D1525 1 |
| Peak Melting Temperature | 186 | °C | ASTM D3418, ISO 3146 |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fainplast PVC HGKA 88/1 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Ferro PP NPP00GE10NA | Ferro Corporation | PP Copolymer | Ferro PP |
| Hytrel® 8238 | DuPont Performance Polymers | TPC-ET | Hytrel® |
| MACOMASS PP MM-PP HI 21 (10% Talc) | MACOMASS Verkaufs AG | PP Homopolymer | MACOMASS PP |
| POLYFLAM® SDR 5005 WHITE 88315 HP25 | A. Schulman Europe | PS (GPPS) | POLYFLAM® |