INFUSE™ 9900
| Category: | OBC , Olefin Block Copolymer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | INFUSE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UdAHLd_INFUSE9900.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INFUSE™ 9900 Olefin Block Copolymer is a high flow olefin elastomer. It is readily formulated for a variety of applications. Main Characteristics:
|
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.880 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 30 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, Injection Molded) | 78 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant 1(Injection Molded) | 4.00 | MPa | ASTM D638 |
| Tensile Strength 2(Break, Injection Molded) | 4.41 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Injection Molded) | 780 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 4(Break) | 5.07 | MPa | ASTM D412 |
| Tensile Elongation 5(Break) | 870 | % | ASTM D412 |
| Tear Strength | 47.5 | kN/m | ASTM D624 |
| Compression Set | ASTM D395 | ||
| 21°C | 38 | % | ASTM D395 |
| 70°C | 98 | % | ASTM D395 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 122 | °C | Internal method |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| 4 . | C mould |
| 5 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pyramid™ PI220 | Polymics, Ltd. | API | Pyramid™ |
| TUFNYL® RGF 33 BLACK | SRF Ltd. | Nylon 66 | TUFNYL® |
| Vydyne® R413H BK07 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| WPP PP PPH4CG-4 | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| NEXT REGRIND PC 143R-300RG | NEXT Specialty Resins, Inc. | PC | NEXT REGRIND |