LEXAN™ SLX2571T resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ud1z7f_LEXAN-SLX2571T-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Transparent weatherable PC copolymer for blowmolding/extrusion. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 3.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 2.70 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 - 0.80 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.35 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2400 | MPa | ASTM D638 |
| -- | 2360 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 62.0 | MPa | ASTM D638 |
| Yield | 63.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 64.0 | MPa | ASTM D638 |
| Fracture | 63.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 7.5 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Fracture 5 | 110 | % | ASTM D638 |
| Fracture | 98 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2400 | MPa | ASTM D790 |
| -- 7 | 2250 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 94.7 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 101 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 15 | kJ/m² | ISO 179/1eA |
| 23°C | 75 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 10(23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| -30°C | 140 | J/m | ASTM D256 |
| 23°C | 850 | J/m | ASTM D256 |
| -30°C 11 | 10 | kJ/m² | ISO 180/1A |
| 23°C 12 | 70 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 13(23°C) | No Break | ISO 180/1U | |
| Instrumented Dart Impact (23°C, Total Energy) | 74.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 126 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 14 | 125 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 143 | °C | ASTM D1525, ISO 306/B50 11 15 |
| -- | 145 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 6.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 6.4E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | V-2 | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 116 - 121 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Cylinder Zone 1 Temp. | 260 - 274 | °C | |
| Cylinder Zone 2 Temp. | 260 - 274 | °C | |
| Cylinder Zone 3 Temp. | 260 - 274 | °C | |
| Cylinder Zone 4 Temp. | 260 - 274 | °C | |
| Cylinder Zone 5 Temp. | 260 - 274 | °C | |
| Adapter Temperature | 260 - 274 | °C | |
| Die Temperature | 268 - 279 | °C |
| Extrusion instructions |
|---|
| Drying Time (Cumulative): 48 hrsHead - Zone 6 - Top Temperature: 260 - 274 °CHead - Zone 7 - Bottom Temperature: 260 - 274 °CMelt Temperature (Parison): 266 - 277 °CMinimum Moisture Content: 0.01 %Mold Temperature: 66 - 93 °CScrew Speed: 15 - 50 rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*3 sp=62mm |
| 10 . | 80*10*3 sp=62mm |
| 11 . | 80*10*3 |
| 12 . | 80*10*3 |
| 13 . | 80*10*3 |
| 14 . | 80*10*4 mm |
| 15 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XCS-2033B | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Ferro PP NPP00GT23NA | Ferro Corporation | PP, Unspecified | Ferro PP |
| Dryflex® A1 602801 | ELASTO | SEBS | Dryflex® |
| Hydrin® T3102 | Zeon Chemicals L.P. | Epoxy | Hydrin® |
| Karina BLACK PVC COMPOUND -E TR-652D48/ 1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |