ZEONEX® E48R
| Category: | COC , Cyclic Olefin Copolymer |
| Manufacturer: | Zeon Corporation |
| Trademark: | ZEONEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ub23ZL_ZEONEX-E48R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ZEONEX® - Cyclo Olefin Polymer (COP) offers excellent optical properties for creating optical parts for cameras and laser beam printers. ZEONEX's high purity is suitable for a wide range of medical packaging products, while its low dielectric constant and loss tangents are appropriate for electrical insulation applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.01 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (280°C/2.16 kg) | 25 | g/10 min | ISO 1133 |
| Water Absorption (Equilibrium) | < 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pencil Hardness | H | JIS K5401 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Injection Velocity | 30.0 to 80.0 | cm³/s | |
| Screw Speed | 20 to 60 | rpm |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ISO 527-2 |
| Tensile Stress | 71.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 10 | % | ISO 527-2 |
| Flexural Modulus | 2500 | MPa | ISO 178 |
| Flexural Stress | 104 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 21 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 122 | °C | ASTM D648 |
| Glass Transition Temperature | 139 | °C | JIS K7121 |
| CLTE - Flow | 6.0E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength 1(1.00 mm) | 40 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 2.30 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 2.0E-4 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.531 | ASTM D542 | |
| Transmittance (3000 µm) | 92.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 4.0 to 10 | hr | |
| Rear Temperature | 260 to 290 | °C | |
| Middle Temperature | 260 to 290 | °C | |
| Front Temperature | 260 to 290 | °C | |
| Mold Temperature | 90.0 to 135 | °C | |
| Injection Pressure | 50.0 to 180 | MPa | |
| Holding Pressure | 50.0 to 180 | MPa | |
| Back Pressure | 5.00 to 10.0 | MPa |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| reSound™ X RS1200-0215 | PolyOne Corporation | PLA Comp | reSound™ |
| Xuchuan XCW-6050NC | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Axiall PVC 12791 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Horda E6595 | Horda Cable Compounds | PE Copolymer | Horda |
| Karina CLEAR PVC COMPOUND 80/202-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |