VESTAMID® NRG 2101 yellow
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | Evonik Industries AG |
| Trademark: | VESTAMID® NRG |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UZgBw2_VESTAMID-NRG-2101-yellow.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
For Gas Pipe Fittings VESTAMID® NRG 2101 yellow is a high molecular grade PA 12 material developed by Evonik. Its superior performance characteristics make it an ideal choice for expanding the use of thermoplastic piping systems at higher operating pressure and larger diameters to replace metallic piping systems in a safe and cost effective manner. Besides extending the operating pressure limits of thermoplastic piping systems, VESTAMID® NRG 2101 yellow offers many of the same benefits, and in most instances more superior performance, as conventional PE piping systems.
We recommend a processing temperature between 230°C (446°F) and 260°C (500°F) in some cases up to 280°C (536°F) - during the injection molding and extrusion process. The mold temperature should be within a range of 60°C (140°F) to 100°C (212°F). Drying at 80°C (176°F) for 2 hours to 4 hours before processing is recommended. Polyamide 12 is a high performance thermoplastic polymer with increased performance characteristics that translates into safe operations over the life of the installed pipeline. It has a considerable record of safe and proven experience in many demanding applications, including fuel lines in passenger cars, air brake tubing in trucks and off-shore applications. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.02 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 73 | ISO 868 | |
| Ball Indentation Hardness 1 | 76.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1350 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 40.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 12 | % | |
| Break | > 150 | % | |
| Hydrostatic Design Basis | |||
| 20°C | 21.7 | MPa | |
| 60°C | 13.8 | MPa | |
| Slow Crack Growth Resistance - 20 bar, 20% notched | > 2000 | hr |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| PENT - 2.4 MPa (80°C) | > 2000 | hr | ASTM F1473 |
| RCP 2 | ISO 13477 | ||
| FST critical pressure : 0°C | 3.00 | MPa | |
| S4 critical pressure : 0°C | 0.270 | MPa | |
| Strength - Maximum Required (20°C) | 18.0 | MPa | ISO 9277 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (-40°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 170 | °C | ISO 306/A |
| Melting Temperature 3 | 177 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 230 to 280 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Melt Temperature | 230 to 280 | °C |
| Note Message | |
|---|---|
| 1 . | H30 |
| 2 . | 110mm SDR 11 |
| 3 . | 2nd Heating |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MBA PP 2117 | MBA Polymers | PP Copolymer | MBA PP |
| Toughblend® PBT-1400 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PBT | Toughblend® |
| Cabofor® 28 GF/20-V0 NATURALE | SO.F.TER. SPA | PC | Cabofor® |
| Evermore PUR SA-2265 | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| Osterlene® HI-13-2.1 | Osterman & Company | PS (HIPS) | Osterlene® |