Starex TX-0510T
| Category: | MABS , Methyl Methacrylate / ABS |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UZOT3f_Starex-TX-0510T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex TX-0510T is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 16 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 109 | ASTM D785 | |
| R-Scale | 110 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 1 | 44.0 | MPa | ASTM D638 |
| Yield | 47.0 | MPa | ISO 527-2/50 |
| Break | 35.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 16 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 2100 | MPa | ASTM D790 |
| -- 3 | 2200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 64.0 | MPa | ASTM D790 |
| -- 5 | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6(23°C) | 13 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 150 | J/m | ASTM D256 |
| 23°C 7 | 12 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 4.00 mm | 83.0 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 86.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 4.00 mm | 70.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 4.00 mm | 80.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 88.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (3200 µm) | 88.0 | % | ASTM D1003 |
| Haze (3200 µm) | 2.8 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 180 to 190 | °C | |
| Middle Temperature | 200 to 210 | °C | |
| Front Temperature | 220 to 230 | °C | |
| Nozzle Temperature | 230 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Pressure | 49.0 to 196 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Thickness: 4 mm |
| 7 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® AS10GR6664 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| NEFTEKHIM PP PP6129K | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| Lucent PC PC/PBT-1020 | Lucent Polymers, Inc. | PC+PBT | Lucent PC |
| Teldene® H06ML | National Petrochemical Industries Company (NATPET) | PP Homopolymer | Teldene® |
| Sylvin 8818-90UV Brown 7386 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |