UNIPA® MRg Datasheet,Nylon 6,Nytef Plastics, Ltd.-SHANGHAI SUSHENG

UNIPA® MRg

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Nytef Plastics, Ltd.
Trademark:	UNIPA®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	UYSBI8_UNIPA-MRg.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Since its introduction in 1938, Nylon has become one of the world's most widely recognized and utilized engineering grade thermoplastics. Nylon's unique combination of high strength, good toughness, outstanding chemical resistance, and excellent wear and abrasion resistance have made it the material of choice for product designs in a multitude of industries. When used to replace wear grade metals like brass and bronze, no other material provides the combination of extended wear life, light weight, and low fabricated part cost of Nylon. Nytef Plastics, Ltd. manufactures UNIPA® Nylon stock shapes in a wide variety of types and stock shape configurations. These UNIPA Nylon products fall into the categories of Type 6/6 Extruded UNIPA Nylons and Type 6 UNIPA M Cast Nylons. While both types of Nylon are very similar, there are performance and availability differences between the two grades that should be noted: UNIPA M Type 6 Cast Nylons: offer improved wear resistance are available in larger rod diameters (up to 13" dia.) are available in larger plate sizes (up to 48" x 96") Nytef Plastics utilizes a proprietary nylon casting process to produce UNIPA M Nylon 6 stock shapes. This process allows Nylon rods, plates, and tubular bars with very thick cross sections to be economically produced with uniform physical properties and minimal internal stress levels. Nytef Plastic's UNIPA M Nylon 6 stock shapes are available in a wide range of grades including lubricated, heat stabilized, and fiber reinforced products. UNIPA M Nylon 6 materials are offered in a complete range of round rod, heavy gauge plate, and tubular bar sizes.

Message

Since its introduction in 1938, Nylon has become one of the world's most widely recognized and utilized engineering grade thermoplastics. Nylon's unique combination of high strength, good toughness, outstanding chemical resistance, and excellent wear and abrasion resistance have made it the material of choice for product designs in a multitude of industries. When used to replace wear grade metals like brass and bronze, no other material provides the combination of extended wear life, light weight, and low fabricated part cost of Nylon. Nytef Plastics, Ltd. manufactures UNIPA® Nylon stock shapes in a wide variety of types and stock shape configurations. These UNIPA Nylon products fall into the categories of Type 6/6 Extruded UNIPA Nylons and Type 6 UNIPA M Cast Nylons. While both types of Nylon are very similar, there are performance and availability differences between the two
grades that should be noted:

UNIPA M Type 6 Cast Nylons:

offer improved wear resistance

are available in larger rod diameters (up to 13" dia.)

are available in larger plate sizes (up to 48" x 96")

Nytef Plastics utilizes a proprietary nylon casting process to produce UNIPA M Nylon 6 stock shapes. This process allows Nylon rods, plates, and tubular bars with very thick cross sections to be economically produced with uniform physical properties and minimal internal stress levels. Nytef Plastic's UNIPA M Nylon 6 stock shapes are available in a wide range of grades including
lubricated, heat stabilized, and fiber reinforced products. UNIPA M Nylon 6 materials are offered in a complete range of round rod, heavy gauge plate, and tubular bar sizes.

General Information
Filler / Reinforcement	Glass Fiber, 30% Filler by Weight
Features	Good Abrasion Resistance Good Chemical Resistance Good Toughness Good Wear Resistance High Stiffness High Strength Machinable
Uses	Automotive Applications Bearings Bushings Construction Applications Electrical Parts Electrical/Electronic Applications Fluid Handling Food Service Applications Gears Mining Applications Molds/Dies/Tools Pulleys Pump Parts Rollers Textile Applications Valves/Valve Parts Wear Strip Wheels
Forms	Preformed Parts Rod

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.28	g/cm³	ASTM D792
Water Absorption			ASTM D570
24 hr	0.40	%
Saturation	3.5	%

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	100		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength	124	MPa	ASTM D638
Tensile Elongation (Break)	8.0	%	ASTM D638
Flexural Strength	172	MPa	ASTM D790
Compressive Strength	172	MPa	ASTM D695
Coefficient of Friction	0.33		ASTM D1894

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	53	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	149	°C	ASTM D648
Continuous Use Temperature	98.9	°C	Internal Method
Peak Melting Temperature	221	°C	ASTM D3418
CLTE - Flow	2.7E-5	cm/cm/°C	ASTM D696

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	> 1.0E+13	ohms·cm	ASTM D257
Dielectric Strength ¹	20	kV/mm	ASTM D149
Dielectric Constant (1 MHz)	3.70		ASTM D150
Dissipation Factor (60 Hz)	0.020		ASTM D150

Flammability	Nominal Value	Unit	Test Method
Flame Rating	HB		UL 94

Note Message
1 .	Method A (Short-Time)

Resin Grade	Manufacturer	Category	Trademark
Maxelast® P3780	Nantong Polymax Elastomer Technology, Co., Ltd	TPE	Maxelast®
Silopren® LSR 3286/50	Momentive Performance Materials Inc.	Silicone Rubber, LSR	Silopren®
TAROPRENE® 1 A70 M1M	Taro Plast S.p.A.	TPV	TAROPRENE®
ADPOLY PH-200	Lotte Chemical Corporation	PP, Unspecified	ADPOLY
Sylvin 8773-60D Brown 7363	Sylvin Technologies Incorporated	PVC, Rigid	Sylvin