LNP™ LUBRICOMP™ RP004 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UVqCKM_LNPLUBRICOMPRP004compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RP004 is a compound based on PA66 resin containing PTFE, Silicone. Added features include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound RL-4540 Product reorder name: RP004 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 1.5 - 2.0 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 63.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 7.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 2500 | MPa | ISO 178 |
| Flexural Stress | 82.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 45 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 64.0 mm Span) | 80.0 | °C | ISO 75-2/Af |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.750 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 293 - 304 | °C | |
| Processing (Melt) Temp | 277 - 288 | °C | |
| Mold Temperature | 82.2 - 93.3 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propylux® Void-Free | Westlake Plastics Company | PP, Unspecified | Propylux® |
| Texalan® 6 Series 682A | Austin Novel Materials Co. Ltd. | TPU-Ester/Ether | Texalan® 6 Series |
| ALCOM® POM 770/1 PTFE1,5 | ALBIS PLASTIC GmbH | Acetal (POM) Copolymer | ALCOM® POM |
| DIC.PPS FZ-2140-D7 | DIC Corporation | PPS | DIC.PPS |
| LNP™ LUBRICOMP™ HAL23 compound | SABIC Innovative Plastics Europe | Nylon 11 | LNP™ LUBRICOMP™ |