UMERIT® 2000F
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | UBE America, Inc. |
| Trademark: | UMERIT® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UTKwhL_UMERIT-2000F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
UBE super polyethylene UMERIT® are ethylene alpha-olefin copolymers produced using metallocene catalyst by gas phase process. The metallocene catalytic method results in superior physical properties by being able to acquire any targeted molecular structures. Therefore UMERIT®2000F offer various excellent properties. -Reduced motor load at processing -Draw resonance at high-speed drawing hardly occurs |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | 4.0 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (F50) | 1000 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 52 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 36.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 760 | % | ASTM D638 |
| Flexural Modulus | 280 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 104 | °C | ASTM D1525 |
| Melting Temperature | 116 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene HP519-00 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Sicostirolo CR G 4142 | Ravago Group | PS (GPPS) | Sicostirolo |
| Celanex® 2104UV | Celanese Corporation | PBT | Celanex® |
| Eleme HIG20060 | Eleme Petrochemical Company Ltd | HDPE | Eleme |
| Karina GRAY PVC COMPOUND 680D18/ 37-CY-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |