Baytec® MS-080 (BDO)
| Category: | PUR-Ester/MDI , Polyurethane (Polyester, MDI) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Baytec® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UTEQn3_Baytec-MS-080-BDO-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Baytec MS-080 modified diphenylmethane diisocyanate (MDI)-terminated polyester prepolymer is used in the manufacture of high-property solid cast polyurethane elastomers. As with any product, use of Baytec MS-080 prepolymer in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Forms |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance (1000 Cycles, 1000 g, H-18 Wheel) | 15.0 | mg | ASTM D4066 |
| Compression Deflection | ASTM D575 | ||
| 10% | 3.03 | MPa | ASTM D575 |
| 15% | 4.24 | MPa | ASTM D575 |
| 2% | 0.586 | MPa | ASTM D575 |
| 20% | 5.45 | MPa | ASTM D575 |
| 25% | 6.76 | MPa | ASTM D575 |
| 5% | 1.65 | MPa | ASTM D575 |
| 50% | 19.9 | MPa | ASTM D575 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 7.58 | MPa | ASTM D412 |
| 200% strain | 11.6 | MPa | ASTM D412 |
| 300% strain | 19.3 | MPa | ASTM D412 |
| Tensile Strength (Break) | 48.3 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 470 | % | ASTM D412 |
| Tear Strength | |||
| -- 1 | 105 | kN/m | ASTM D624 |
| Cracking | 56 | kN/m | ASTM D1938 |
| Compression Set (70°C, 22 hr) | 15 | % | ASTM D395 |
| Bayshore Resilience | 50 | % | ASTM D2632 |
| Additional Information |
|---|
| Appearance: White to cream solidNCO: 8.1 to 8.5 wt%Flash Point, PMCC: 224°CSpecific Gravity at 80°C: 1.12Specific Gravity at 100°C: 1.11Viscosity at 80°C: 1210 mPa-sViscosity at 100°C: 590 mPa-sNCO/OH Ratio: 1.05Stoichiometry: 95% TheoryPrepolymer Temperature: 80 to 90°CExtender Temperature: 25 to 70°CMold Temperature: 90 to 110°CPot Life: 2 to 4 minDemold: 30 min |
| Note Message | |
|---|---|
| 1 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPV X10085B | Teknor Apex Company | TPV | Sarlink® TPV |
| Vistalon™ 9301 | ExxonMobil Chemical | EPDM | Vistalon™ |
| Ebalta MG 815 / Comp. A+B | Ebalta Kunststoff GmbH | PUR, Unspecified | Ebalta |
| Elastron® V V250.A65.B | Elastron USA, Inc. | TPV | Elastron® V |
| 3M™ Dyneon™ PTFE Compound PDR 010031 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |