Electrafil® PBT GF10 SS5 MB
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Electrafil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | USz4e8_Electrafil-PBT-GF10-SS5-MB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Electrafil® PBT GF10 SS5 MB is a Polybutylene Terephthalate (PBT) product filled with 10% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.90 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.080 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 49.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 7.0 | % | ASTM D638 |
| Flexural Modulus | 3520 | MPa | ASTM D790 |
| Flexural Strength | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 48 | J/m | ASTM D256 |
| Unnotched Izod Impact | 800 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 108 | °C | ASTM D648 |
| CLTE - Flow | 4.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+6 to 1.0E+9 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+6 to 1.0E+9 | ohms·cm | ASTM D257 |
| Static Decay | < 2.0 | sec | MIL PRF-81705D |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 232 to 274 | °C | |
| Middle Temperature | 232 to 274 | °C | |
| Front Temperature | 232 to 274 | °C | |
| Processing (Melt) Temp | 232 to 246 | °C | |
| Mold Temperature | 65.6 to 82.2 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6000/50 HWUVCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Nucrel® 0403 | DuPont Packaging & Industrial Polymers | EMAA | Nucrel® |
| Boltaron 3060 TruPrint | Boltaron Performance Products | PVC, Rigid | Boltaron |
| Lupoy® 1302-10 | LG Chem Ltd. | PC | Lupoy® |
| Deprene 101-55 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PP+EPDM | Deprene |