Lion Idemitsu Composites PPS G531F3
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Lion Idemitsu Composites Co., Ltd. |
| Trademark: | Lion Idemitsu Composites PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | USGm23_Lion-Idemitsu-Composites-PPS-G531F3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lion Idemitsu Composites PPS G531F3 is a Polyphenylene Sulfide (PPS) product filled with 30% glass fiber. It is available in Asia Pacific. Primary characteristic: lubricated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.68 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow | 0.60 | % | |
| Flow | 0.50 | % | |
| Water Absorption (23°C, 24 hr) | > 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 92 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.8 | % | ISO 527-2 |
| Flexural Modulus | 11700 | MPa | ISO 178 |
| Flexural Stress | 226 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 9.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 265 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 1.6E-5 | cm/cm/°C | |
| Transverse | 5.3E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Constant | 3.60 | IEC 60250 | |
| Dissipation Factor | 1.9E-3 | IEC 60250 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flowability 2(1.00 mm) | 136 | mm | Internal Method |
| Note Message | |
|---|---|
| 1 . | Internal Method |
| 2 . | Thickness 1mm, Cylinder temperature 320°C, Injection pressure 100MPa, Mold temperature 135°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC7HAZ (Series: AD/POM) | KRAIBURG TPE | TPE | THERMOLAST® K |
| THORNEL® GPC-10 | Cytec Industries Inc. | Carbon/Epoxy | THORNEL® |
| ELASTOSIL® P 7636 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® P |
| Karina NATURAL PVC COMPOUND -E 550-25/ 1-AY-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 9604A-95 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |