RTP 799 X 143519 EG
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | URrskF_RTP799X143519EG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ESD Protection - Permanently Static Dissipative - Extrusion Grade |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.960 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | < 1.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 2.0 - 4.0 | % | ASTM D955 |
| Moisture Content | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Static Decay | sec | FTMS 101C 4046.1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 414 | MPa | ASTM D638 |
| Tensile Strength | 15.9 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 10 | % | ASTM D638 |
| Flexural Modulus | 483 | MPa | ASTM D790 |
| Flexural Strength | 15.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | No Break | ASTM D4812 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+8 - 1.0E+10 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+7 - 1.0E+9 | ohms·cm | ASTM D257 |
| Injection instructions |
|---|
| Do not exceed 520 °F (270 °C) melt temperature.Desiccant Type Dryer Required. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79 | °C | |
| Drying Time | 2.0 | hr | |
| Melt Temperature | 182 - 216 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROLOX 111 G3 | Taro Plast S.p.A. | PET | TAROLOX |
| 4LEX® 10F13300 | 4Plas | PC | 4LEX® |
| AIE PA6 50G6 | Asia International Enterprise (Hong Kong) Limited | Nylon 6 | AIE PA6 |
| Celstran® TPU-GF60-01 | Celanese Corporation | TPU, Unspecified | Celstran® |
| LNP™ LUBRICOMP™ OCP36 compound | SABIC Innovative Plastics | PPS | LNP™ LUBRICOMP™ |