RTP 4787
| Category: | PTT , Polytrimethylene Terephthalate |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UPrELX_RTP-4787.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Carbon Fiber |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | < 0.050 | % | ASTM D955 |
| Moisture Content | 0.010 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 29000 | MPa | ASTM D638 |
| Tensile Strength | 172 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 1.0 - 2.0 | % | ASTM D638 |
| Flexural Modulus | 24800 | MPa | ASTM D790 |
| Flexural Strength | 255 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 48 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 590 | J/m | ASTM D4812 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 127 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Dew Point | -40.0 | °C | |
| Processing (Melt) Temp | 232 - 260 | °C | |
| Mold Temperature | 87.8 - 121 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAXALEN™ PPC343G20 | SAX Polymers | PP Copolymer | SAXALEN™ |
| SOLARENE H663 | Dongbu Hannong Chemical | PS (HIPS) | SOLARENE |
| Huafon T25P | Huafon Group Co., Ltd. | Nylon 66 | Huafon |
| Petrothene® XL07505 | LyondellBasell Industries | EVA | Petrothene® |
| LEXAN™ 925 resin | SABIC Innovative Plastics | PC | LEXAN™ |