TRIBOCOMP® PA66 CF30 TS12
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | EPIC Polymers |
| Trademark: | TRIBOCOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UOOggz_TRIBOCOMP-PA66-CF30-TS12.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRIBOCOMP® PA66 CF30 TS12 is a Polyamide 66 (Nylon 66) product filled with 30% carbon fiber. It is available in Europe. Primary characteristic: wear resistant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.28 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.20 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.8 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| 23°C | 21000 | 16500 | MPa | |
| 90°C | 14000 | -- | MPa | |
| 120°C | 10000 | -- | MPa | |
| Tensile Stress | ISO 527-2 | |||
| Yield, 23°C | 260 | 205 | MPa | |
| Yield, 90°C | 150 | -- | MPa | |
| Yield, 120°C | 125 | -- | MPa | |
| Tensile Strain (Break, 23°C) | 2.0 | 3.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 19000 | -- | MPa | ISO 178 |
| Flexural Stress (23°C) | 380 | 285 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | -- | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 40 | -- | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 255 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 253 | -- | °C | ISO 75-2/A |
| CLTE - Flow (23°C) | 2.1E-5 | -- | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.51 | -- | W/m/K | ISO 22007 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+2 | -- | ohms | ASTM D257 |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 270 to 300 | °C | |
| Cylinder Zone 2 Temp. | 275 to 295 | °C | |
| Cylinder Zone 3 Temp. | 280 to 295 | °C | |
| Cylinder Zone 4 Temp. | 290 to 310 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polymer-E V26061 | Asia Polymer Corporation (APC) | EVA | Polymer-E |
| Monprene® OM-12248 | Teknor Apex Company | TPE | Monprene® |
| Axiall PVC 6704 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| CONAP® AD-7410 | Cytec Industries Inc. | Epoxy | CONAP® |
| Latigea B01 I8 | LATI S.p.A. | PLA | Latigea |