Trexprene® A80NU
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Mitsubishi Chemical Performance Polymers, Inc. |
| Trademark: | Trexprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UNhCUr_Trexprene-A80NU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Product Description: TREXPRENE ® A80NU is a heat stabilized PP/EPDM based Thermoplastic Vulcanized Elastomer (TPV). This Natural compound is intended primarily for underhood applications such as mats, seals, gaskets, air ducts, CVJ boots, covers, grommets or other parts where softness and conformity are needed. This material can be processed using Injection Molding, Extrusion, Blow Molding or other melt processing techniques. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.940 to 1.00 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A | 80 to 86 | ||
| Shore A, 15 sec | 77 to 83 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ISO 37 | ||
| Across Flow : 100% Strain | 4.00 | MPa | |
| Flow : 100% Strain | 5.70 | MPa | |
| Tensile Stress 2 | ISO 37 | ||
| Across Flow : Break | 9.30 | MPa | |
| Flow : Break | 8.30 | MPa | |
| Tensile Elongation 3 | ISO 37 | ||
| Across Flow : Break | 750 | % | |
| Flow : Break | 480 | % | |
| Tear Strength 4 | ISO 34-1 | ||
| Across Flow | 37 | kN/m | |
| Flow | 38 | kN/m | |
| Compression Set | |||
| 70°C, 22 hr | 43 | % | ASTM D395B |
| 125°C, 70 hr | 57 | % | ASTM D395B |
| 70°C, 22 hr 5 | 43 | % | ISO 815 |
| 125°C, 70 hr 6 | 57 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air | ISO 188 | ||
| 135°C, 1000 hr | -2.0 | % | |
| 150°C, 168 hr | -7.4 | % | |
| Change in Tensile Strain at Break in Air | ISO 188 | ||
| 135°C, 1000 hr | -12 | % | |
| 150°C, 168 hr | -15 | % | |
| Change in Tensile Stress (125°C, 70 hr, in IRM 903 Oil) | -37 | % | ISO 1817 |
| Change in Tensile Strain at Break (125°C, 70 hr, in IRM 903 Oil) | -57 | % | ISO 1817 |
| Change in Volume (125°C, 70 hr, in IRM 903 Oil) | 78 | % | ISO 1817 |
| Change in Tear Strength - 70 hrs, in IRM 903 Oil (125°C) | -58 | % | ISO 1817 |
| Change in Tensile Properties | |||
| Stress at 100% Elongation in Air, 168 hrs : 150°C | 12 | % | ISO 188 |
| Stress at 100% Elongation in IRM 903 Oil, 70 hrs : 125°C | -8.0 | % | ISO 1817 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Ozone Resistance (40°C) 7 | 0 Rating | ISO 1431-1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | |||
| -- | -59.0 | °C | ASTM D746 |
| Type B | -59.0 | °C | ISO 812 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 26 | mm/min | ISO 3795 |
| Note Message | |
|---|---|
| 1 . | Type 1, 500 mm/min |
| 2 . | Type 1, 500 mm/min |
| 3 . | Type 1, 500 mm/min |
| 4 . | Method Ba, Angle (Unnicked), 500 mm/min |
| 5 . | Type A |
| 6 . | Type A |
| 7 . | 100 pphm, Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SITRALON 18E-TF10-HK / C7043 Dark Grey | SITRAPLAS GmbH | PC | SITRALON |
| Taitacell EPS 301S | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| Aquivion® PW87S | Solvay Specialty Polymers | PFSA | Aquivion® |
| Lucky Enpla LMA1000 | Lucky Enpla Co LTD | Acrylic (PMMA) | Lucky Enpla |
| MAXATEL® ACGC25A-NAT | Pier One Polymers, Inc. | Acetal (POM) Copolymer | MAXATEL® |