INSULCAST® 118 FC
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | ITW Polymers Coatings North America |
| Trademark: | INSULCAST® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UNWRLz_INSULCAST-118-FC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| INSULCAST 118 FC is an equal ratio by weight of volume epoxy potting/casting compound designed for dispensing equipment. INSULCAST 118 FC exhibits good impact strength and mechanical shock resistance. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore D) | 70 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 65.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 to 5.0 | % | ASTM D638 |
| Compressive Strength | 86.2 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE - Flow | 4.8E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.65 | W/m/K | |
| Service Temperature | 105 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 16 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 3.70 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 0.010 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Volume: 1.0 Mix Ratio by Weight: 1.0 | ||
| Part B | Mix Ratio by Volume: 1.0 Mix Ratio by Weight: 1.0 | ||
| Shelf Life (25°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 1 | Black | ||
| -- 2 | Grey | ||
| Density | |||
| -- 3 | 1.52 | g/cm³ | |
| -- 4 | 1.52 | g/cm³ | |
| Viscosity | ASTM D2393 | ||
| -- 5 | 5.0 | Pa·s | |
| -- 6 | 5.5 | Pa·s | |
| -- 7 | 6.0 | Pa·s | |
| Curing Time (25°C) | 12 to 16 | hr | |
| Pot Life (25°C) | 60 | min |
| Note Message | |
|---|---|
| 1 . | Part A |
| 2 . | Part B |
| 3 . | Part B |
| 4 . | Part A |
| 5 . | Part A |
| 6 . | Mixed |
| 7 . | Part B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stylac™ T8701 | Asahi Kasei Chemicals Corporation | AS | Stylac™ |
| Ultramid® 66 H2 G/35-V0KB1 BK3324 | BASF Corporation | Nylon 66 | Ultramid® |
| Badamid® B70 GF50 | Bada AG | Nylon 6 | Badamid® |
| Plaslube® POM CO TS20 LE | Techmer Engineered Solutions | Acetal (POM) Copolymer | Plaslube® |
| POCAN® B 1700 000000 | LANXESS GmbH | PBT | POCAN® |