Resilience™ LS11150E
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Resilience™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UM4ltC_ResilienceLS11150E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Resilience™LS11150E is a rigid polyvinyl chloride product,. It can be processed by extrusion and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: lighting equipment. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792 |
| PVC Cell Classification | 12474 | ASTM D1784 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 81 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 4720 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 54.8 | MPa | ASTM D638 |
| Flexural Modulus | 4540 | MPa | ASTM D790 |
| Flexural Strength | 95.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Compression Molded) | 43 | J/m | ASTM D256A |
| Drop Impact Resistance | ASTM D4226 | ||
| 23°C 3 | 53.4 | J/cm | ASTM D4226 |
| 23°C 4 | 53.4 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, annealed 5 | 78.9 | °C | ASTM D648 |
| 0.45 MPa, annealed, 3.18mm 6 | 77.2 | °C | ASTM D648 |
| 1.8 MPa, annealed 7 | 77.0 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm 8 | 73.9 | °C | ASTM D648 |
| CLTE - Flow | 4.6E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.9 to 3.0mm, gray 2482) | 5VA | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 182 - 193 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| 3 . | Procedure A, C.125 Throwing |
| 4 . | Procedure B, C.125 Throwing |
| 5 . | Annealed at 60 deg.C |
| 6 . | Annealed at 50 deg.C |
| 7 . | Annealed at 60 deg.C |
| 8 . | Annealed at 50 deg.C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TABOREX TA 2385 HD | SILON s.ro | TP, Unspecified | TABOREX |
| Elastron® G G400.A22.N | Elastron USA, Inc. | SEBS | Elastron® G |
| KumhoSunny ABS HFA705 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
| Lumiflon® LF-710F | Asahi Glass Co., Ltd. | Fluoropolymer | Lumiflon® |
| Lucky Enpla LPC1006SG | Lucky Enpla Co LTD | PC | Lucky Enpla |