| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | RIALTI Srl |
| Trademark: | E-RIALFILL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ULldgH_E-RIALFILL-H-15-SJ-40-C1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyproplene homopolymer obtained by recycling of industrial scraps, 42% filled with calcium carbonate, thermal stabilization of process and for contact detergent solution. Flowability specifc for injection molding; good stiffness, good superficial aesthetic and thermal properties; available in natural and colored as per sample. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.26 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 11 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.0 | % | |
| Flow | 1.0 | % | |
| Water Absorption 1(23°C, 24 hr) | 0.020 | % | ISO 62 |
| Ash Content | 42 | % | ISO 3451 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Oven Aging (150°C) | > 20.8 | day | ISO 4577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 74 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/20 | ||
| Yield, 23°C | 22.0 | MPa | |
| Break, 23°C | 17.0 | MPa | |
| Tensile Strain | ISO 527-2/20 | ||
| Yield, 23°C | 15 | % | |
| Break, 23°C | 100 | % | |
| Flexural Modulus 2(23°C) | 2400 | MPa | ISO 178 |
| Flexural Stress (23°C) | 34.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 37 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 2.9 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 58.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 93.0 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 335 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 200 to 220 | °C | |
| Mold Temperature | 40.0 to 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50%RH |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 5701P | SABIC Americas, Inc. | PP Homopolymer | SABIC® PP |
| MonoSol® M7031 | MonoSol, LLC | PVOH | MonoSol® |
| Durethan® DP 1441/40 H3.0 EF 000000 | LANXESS Corporation | Nylon 6 | Durethan® |
| Petrotene® PP A3 T40 BRCA005 PH322 | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |
| Plenco 08112 (Compression) | Plastics Engineering Co. | Polyester, TS | Plenco |