SCHULABLEND® M/MB 6301
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULABLEND® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ULW1fL_SCHULABLENDMMB6301.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ABS/PC-blend with higher impact and heat resistance |
| General Information | |
|---|---|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 16.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2260 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/50 | ||
| Yield | 55.0 | MPa | ISO 527-2/1A/50 |
| Fracture | 40.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain | ISO 527-2/1A/50 | ||
| Yield | 5.2 | % | ISO 527-2/1A/50 |
| Fracture | 40 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 17 | kJ/m² | ISO 179/1eA |
| -20°C | 17 | kJ/m² | ISO 179/1eA |
| 23°C | 45 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| -20°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 127 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 105 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 140 | °C | ISO 306/A50 |
| -- | 129 | °C | ISO 306/B50 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Regrind | 20 | % | |
| Hopper Temperature | 70 | °C | |
| Rear Temperature | 230 | °C | |
| Middle Temperature | 255 | °C | |
| Front Temperature | 280 | °C | |
| Processing (Melt) Temp | 260 - 270 | °C | |
| Mold Temperature | 70 - 90 | °C | |
| Injection Pressure | 100 - 150 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 30.0 - 75.0 | MPa | |
| Back Pressure | 4.00 - 7.00 | MPa | |
| Cushion | 2.00 - 5.00 | mm | |
| Screw Speed | mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEETEC LDPE XJ800 | Lotte Chemical Corporation | LDPE | SEETEC LDPE |
| Sindustris PP HM3208SM | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Axiall PVC 12812 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Conpol™ 20S2 | DuPont Packaging & Industrial Polymers | EMAA | Conpol™ |
| Sylvin 5170-85 White 1535 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |