ALPHALAC SG910
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | ALPHALAC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ULEHhg_ALPHALAC-SG910.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| lphalac of LG chemical is high functionality styrene resin and offers excellent properties and processibility .This product can be accepted as the replacement of general ABS resins. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 3.7 | g/10 min | |
| 220°C/10.0 kg | 40 | g/10 min | |
| 230°C/3.8 kg | 10 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 102 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 34.3 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 38 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2230 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 52.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.40 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 82.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | HB | ||
| 3.18 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Rear Temperature | 170 to 190 | °C | |
| Middle Temperature | 180 to 200 | °C | |
| Front Temperature | 190 to 210 | °C | |
| Nozzle Temperature | 190 to 220 | °C | |
| Processing (Melt) Temp | 190 to 220 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C | |
| Back Pressure | 29.4 to 58.8 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME GPPS SC203E | Supreme Petrochem Ltd. | PS (GPPS) | SUPREME GPPS |
| Anjacom® 055/80-GFK 5/15 Natural | Almaak International GmbH | PC+ABS | Anjacom® |
| ColorRx® PC-2500RXR | LTL Color Compounders, Inc. | PC | ColorRx® |
| HOPELEX PCH-2006 | Lotte Chemical Corporation | PC | HOPELEX |
| PLANAC BT-3500 | TOYOBO America, Inc. | PBT | PLANAC |