GLS ABS NN09
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | GLS Polymers Pvt. Ltd. |
| Trademark: | GLS ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UIid5r_GLS-ABS-NN09.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ABS HR1 (Heat Resistance) Precolor |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 to 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 6.0 to 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 45.0 to 52.0 | MPa | ASTM D638 |
| Flexural Modulus 2 | 2300 to 2450 | MPa | ASTM D790 |
| Flexural Strength 3 | 75.0 to 82.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 120 to 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 106 to 108 | °C | ASTM D648 |
| Vicat Softening Temperature | 125 to 127 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 206 to 236 | °C | |
| Mold Temperature | 65.0 to 86.0 | °C | |
| Injection Pressure | 70.0 to 101 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP548R | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Ad-Tech Urethanes UC-4685 | Ad-Tech Plastic Systems Corp. | TSU | Ad-Tech Urethanes |
| APEL™ APL5514ML | Mitsui Chemicals America, Inc. | COC | APEL™ |
| Daelim Po1y® DHC-1 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| LEXAN™ 9915A_ resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |