TEKNIFLEX® VDC 300-40
| Category: | Film, PVC/PVDC , PVC/PVDC Film |
| Manufacturer: | Tekni-Films, a div of Tekni-Plex |
| Trademark: | TEKNIFLEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UHH9o2_TEKNIFLEX-VDC-300-40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermoformable, FDA-compliant, Pharmaceutical-Grade PVC/PVdC film lamination. Tekni-Plex Plex offers a wide range of PVC-based film structures to meet both performance and cost requirements. |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | |
| Dimensional Stability 1(140°C) | -4.0 to 4.0 | % |
| Films | Nominal Value | Unit | |
|---|---|---|---|
| Film Thickness 2 | 323 | µm | |
| Yield | 2.22 | m²/kg |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Roll Width 3 | < 130.00 | cm | |
| Thermoforming Molding Temperature | 100 to 160 | °C |
| Films | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength - MD (Yield) | 41.4 | MPa | |
| Oxygen Transmission Rate (23°C, 50% RH) | 0.65 | cm³/m²/24 hr | |
| Water Vapor Transmission Rate (38°C, 90% RH) | 0.60 | g/m²/24 hr |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Haze | 5.0 | % |
| Note Message | |
|---|---|
| 1 . | 30 minutes |
| 2 . | Thickness tolerance: ±7% |
| 3 . | Roll width tolerance: ±1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Styrolution PS 1621 | INEOS Styrolution Group GmbH | PS (GPPS) | Styrolution PS |
| Nycal™ 2150R25F1 | Technical Polymers, LLC | Nylon 66 | Nycal™ |
| AMPLIFY™ IO 3801 | The Dow Chemical Company | Ionomer | AMPLIFY™ IO |
| DESOX™ DSC401GM9 | DESCO Co., Ltd. | PBT | DESOX™ |
| Karina PINK PVC COMP -E KAPU 6539/380-NT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |