Polylink Polymer PBT-11030-GF

Category:	PBT , Polybutylene Terephthalate
Manufacturer:	Polylink Polymers (India) Ltd.
Trademark:	Polylink Polymer
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	UGrDV0_Polylink-Polymer-PBT-11030-GF.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Filled PBT compounds are manufacturedbycom pounding PBT with specially treated choppedglass and modified with additives to make parts withhigh mechanical properties, heat resistance and fire resistance.

Excellent flame retardancy.

Good resistance to environmental stress-cracking.

High heat deflection temperature.

Low warpage.

Good mould release.

Good Mechanical Properties.

General Information
Filler / Reinforcement	Filler, 30% filler by weight
Features	Low warpage High ESCR (Stress Cracking Resistance) Good demoulding performance Flame retardancy
Appearance	Natural color

Physical	Nominal Value	Unit	Test Method
Density	1.55 - 1.62	g/cm³	Internal method
Moisture Content	< 800	ppm	Internal method

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Break)	108 - 118	MPa	ASTM D638
Flexural Modulus	8240 - 8430	MPa	ASTM D790
Flexural Strength	167 - 177	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	64 - 74	J/m	ASTM D256

Extrusion	Nominal Value	Unit
Drying Temperature	80.0 - 100	°C
Drying Time	2.0 - 4.0	hr
Cylinder Zone 1 Temp.	215	°C
Cylinder Zone 2 Temp.	220	°C
Cylinder Zone 3 Temp.	230	°C
Cylinder Zone 4 Temp.	240	°C
Cylinder Zone 5 Temp.	245	°C

Extrusion instructions
Zone 6 : 250°C

Resin Grade	Manufacturer	Category	Trademark
Nylex™ 4650	Multibase, A Dow Corning Company	Nylon+PP	Nylex™
HiFill FR® PC GF10 FR BK	Techmer Engineered Solutions	PC	HiFill FR®
IDI SMC S10 (Glass Content 20%)	IDI Composites International	TS, Unspecified	IDI SMC
PELPRENE™ S2002FB	TOYOBO America, Inc.	TPEE	PELPRENE™
ULTEM™ 1010R resin	SABIC Innovative Plastics	PEI	ULTEM™