LNP™ STAT-KON™ MFD02 compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UGGtxP_LNPSTATKONMFD02compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON MFD02 is a compound based on Polypropylene resin containing Glass Fiber, Carbon Powder. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound MF-10 Product reorder name: MFD02 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 1.1 - 1.3 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.1 - 1.3 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 1.2 | % | ISO 294-4 |
| Flow direction : 24 hours | 1.2 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2760 | MPa | ASTM D638 |
| -- | 2430 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 28.3 | MPa | ASTM D638 |
| Yield | 28.0 | MPa | ISO 527-2 |
| Fracture | 20.7 | MPa | ASTM D638 |
| Fracture | 23.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 3.2 | % | ASTM D638 |
| Yield | 2.9 | % | ISO 527-2 |
| Fracture | 6.1 | % | ASTM D638 |
| Fracture | 4.2 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2070 | MPa | ASTM D790 |
| -- | 2200 | MPa | ISO 178 |
| Flexural Stress | 43.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C 2 | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 380 | J/m | ASTM D4812 |
| 23°C 3 | 28 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 16.7 | J | ASTM D3763 |
| -- | 11.9 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 134 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 127 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 85.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 81.0 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 1.0E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 6.5E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 6.4E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 - 1.0E+3 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 - 204 | °C | |
| Middle Temperature | 216 - 227 | °C | |
| Front Temperature | 238 - 249 | °C | |
| Processing (Melt) Temp | 227 - 249 | °C | |
| Mold Temperature | 32.2 - 48.9 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® Vestolen A 6060R 10000 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® Vestolen A |
| NEFTEKHIM PP 8345R | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| GLAMIDE® TY-181GC | TOYOBO America, Inc. | Nylon 6 Elast | GLAMIDE® |
| DOW™ HDPE DMDD-1210 NT 7 | The Dow Chemical Company | HDPE | 陶氏高密度聚乙烯 |
| Daelim Po1y® VL0001 | DAELIM INDUSTRIAL CO., LTD. | Plastomer | Daelim Po1y® |