Sarlink® TPE ME-2640DB BLK (PRELIMINARY DATA)
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UG8gho_Sarlink-TPE-ME-2640DB-BLK-PRELIMINARY-DATA-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sarlink ME-2640DB is a high flow, high hardness molding grade with UV resistance, for automotive exterior applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.937 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Injection Molded) | 38 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress - Across Flow (100% Strain) | 8.10 | MPa | ISO 37 |
| Tensile Strength - Across Flow (Break) | 15.9 | MPa | ISO 37 |
| Tensile Elongation - Across Flow (Break) | 720 | % | ISO 37 |
| Compression Set (70°C, 22 hr) | 78 | % | ISO 815 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Shear Viscosity - Capillary, 206 1/s (200°C) | 174 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 170 - 180 | °C | |
| Middle Temperature | 180 - 200 | °C | |
| Front Temperature | 200 - 220 | °C | |
| Nozzle Temperature | 210 - 230 | °C | |
| Processing (Melt) Temp | 200 - 230 | °C | |
| Mold Temperature | 10.0 - 60.0 | °C | |
| Injection Pressure | 6.00 - 12.0 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 4.00 - 6.00 | MPa | |
| Back Pressure | 0.500 - 2.00 | MPa | |
| Screw Speed | 50 - 120 | rpm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets 2 to 4 hours at 65 degrees Celsius.Time Settings:Injection time: 0.5-2 secondsHolding time: 1-10 secondsCooling time: As short as possible. The parts should be removable without deformation or piercing of the ejector(s) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 66 MV HI | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| Sylvin 8260-60 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| HiFill FR® ABS/PBT FR | Techmer Engineered Solutions | ABS+PBT | HiFill FR® |
| Karina MBPEB WHITE -E 1000/3055-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| KMI PP KM-003IB | KMI Group, Inc. | PP Impact Copolymer | KMI PP |