LUVOCOM® 3-8269/BL Datasheet,Nylon 6,LEHVOSS Group-SHANGHAI SUSHENG

Message
LUVOCOM®3-8269/BL is a polyamide 6 (nylon 6) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main characteristics of 3-8269/BL are: wear resistance. Typical application areas include: engineering/industrial accessories Tools container textile/fiber Automotive Industry

General Information
Features	Low friction coefficient Good wear resistance
Uses	Textile applications Engineering accessories Machine/mechanical parts Mould Application in Automobile Field Container Food container Mold/Mold/Tool
Appearance	Blue

Physical	Nominal Value	Unit	Test Method
Density	1.69	g/cm³	ISO 1183
Molding Shrinkage	1.1 - 1.5	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 1.0	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	4500	MPa	ISO 527-2
Tensile Stress (Break)	65.0	MPa	ISO 527-2
Tensile Strain (Yield)	2.3	%	ISO 527-2
Flexural Modulus	3800	MPa	ISO 178
Flexural Stress	90.0	MPa	ISO 178
Flexural Strain at Flexural Strength	3.0	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	120	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	> 1.0E+10	ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	3.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	30	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Continuous Use Temperature	80.0	°C	UL 746B

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+10	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying Temperature
Hot air dryer, A	75	°C
Hot air dryer, B	105	°C
Drying Time
Hot air dryer, A	10 - 16	hr
Hot air dryer, B	4.0 - 6.0	hr
Rear Temperature	250 - 270	°C
Middle Temperature	270 - 290	°C
Front Temperature	280 - 300	°C
Nozzle Temperature	270 - 280	°C
Processing (Melt) Temp	270	°C
Mold Temperature	70 - 110	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Category:	Nylon 6 , Polyamide 6
Manufacturer:	LEHVOSS Group
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	UFqmB7_LUVOCOM38269BL.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
TAISOX 2110	Formosa Plastics Corporation	LLDPE	TAISOX
TAFMER™ A-1050S	Mitsui Chemicals America, Inc.	PAO	TAFMER™
Celanex® 5202	Celanese Corporation	PBT	Celanex®
Mafill® HT 4210	Ravago Group	PP Homopolymer	Mafill®
Geon™ Vinyl Flexible HC38580	PolyOne Corporation	PVC, Flexible	Geon™ Vinyl Flexible