Ferro PP TPP10AE14NA
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ferro Corporation |
| Trademark: | Ferro PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UFVqLy_Ferro-PP-TPP10AE14NA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ferro PP TPP10AE14NA is a polypropylene homopolymer (PP Homopoly) material, which contains 12% talc filler. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is injection molding. The main characteristics of Ferro PP TPP10AE14NA are: homopolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.988 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.5 | % | ASTM D955 |
| Transverse flow | 1.8 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 36.5 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 10 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% secant : 23°C | 2000 | MPa | ASTM D790 |
| Tangent : 23°C | 2280 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 55.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 48 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 530 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 121 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 82.2 | °C | ASTM D648 |
| Additional Information |
|---|
| The value listed as Unnotched Izod Impact, ASTM D256, was tested in accordance with ASTM D4812. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 204 - 210 | °C | |
| Middle Temperature | 210 - 213 | °C | |
| Front Temperature | 213 - 216 | °C | |
| Nozzle Temperature | 216 - 218 | °C | |
| Mold Temperature | 43.3 - 54.4 | °C | |
| Back Pressure | 0.138 - 0.345 | MPa | |
| Screw Speed | 100 - 150 | rpm | |
| Clamp Tonnage | 2.8 - 4.1 | kN/cm² | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarnamid® T-27 GF 140 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| ULTEM™ AR9300 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| DJSilicone NE-9450 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| DJSilicone NE-9460 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Polifil® Nylon 82MR | The Plastics Group | Nylon 6 | Polifil® Nylon |